Mechanical damage characterization of glass fiber-reinforced polymer laminates by ultrasonic maps

A method for simultaneous measurement of the thickness and density for Glass Fiber-Reinforced Polymer (GFRP) laminate plates with ultrasonic waves in C-Scan mode is presented in the form of maps. The method uses three different signals in immersion pulse-echo C-Scan mode. The maps obtained based on the density show the heterogeneity of the material at high resolution at the pixel level (1 × 1 mm²) and therefore they represent an efficient tool to assess and evaluate the damage of the composite structures after manufacturing and after an applied mechanical loading.     

A methodology for the estimation of transverse failure strength of an oxidized lamina from isothermal aging studies

Surface oxidation and ensuing damage substantially decrease the service life of High Temperature Polymer Matrix Composite (HTPMC) structures. Oxidative degradation behavior of composites is strongly dependent on the coupling between chemical and mechanical responses of the material. In a composite lamina, the onset of damage and subsequent coupled acceleration of both damage and oxidation are controlled by the transverse failure strength of the oxidized regions. The direct measurement of this strength from experimentation is challenging and cumbersome. A model-based methodology for estimating the mean transverse failure strength of the oxidized regions of a unidirectional composite is described in this paper. As the strength of the oxidized region is expected to show a high-degree of spatial variability, the estimated mean is shown to be relatively insensitive to the effect of strength variance. The developed methodology is illustrated with isothermal aging data available for a typical high-temperature composite system.     

Synergistic effect of co-alloying elements on site preferences and elastic properties of Ni3Al: A first-principles study

The site preferences of co-alloying elements (Mo–Ta, Mo–Re, Mo–Cr) in Ni₃Al are studied using first-principles calculations, and the effects of these alloying elements on the elastic properties of Ni₃Al are evaluated by elastic property calculations. The results show that the Mo–Ta, Mo–Re and Mo–Cr atom pairs all prefer Al–Al sites and the spatial neighbor relation of substitution sites almost has no influence on the site preference results. Furthermore, the Young's modulus of Ni₃Al increases much higher by substituting Al–Al sites with co-alloying atoms, among which Mo–Re has the best strengthening effect. The enhanced chemical bondings between alloying atoms and their neighbor host atoms are considered to be the main strengthening mechanism of the alloying elements in Ni₃Al.     

Iterative equalization combining algorithm in intersymbol interference channel

To realize joint optimization of spatial diversity and equalization combining in the intersymbol interference (ISI) channel, an iterative equalization combining algorithm is proposed. The proposed algorithm uses the coefficients of Turbo equalization to calculate the combination weights without estimating the signal to noise ratio in each diversity branch. The equalized symbols from different diversity branches are combined, and the extrinsic information output from the decoder is fed back to the equalizers, so as to exchange soft information between the equalizers and the decoder. The performance of the proposed algorithm is analyzed using the extrinsic information transfer (EXIT) chart and verified by simulations. Results show that our approach fully exploits time domain information from the multipath channel and spatial domain information from multi receiving antennas, which efficiently improve the performance of the receiver in the severe ISI channel.     

In-situ TEM observation of structural changes in nano-crystalline CoCrCuFeNi multicomponent high-entropy alloy (HEA) under fast electron irradiation by high voltage electron microscopy (HVEM)

The structural changes induced in a CoCrCuFeNi multicomponent nano-crystalline high-entropy alloy (HEA) under fast electron irradiation were investigated by in-situ transmission electron microscopy (TEM) using a high voltage electron microscope (HVEM). A fine-grained face centered cubic (fcc) single phase was obtained in the sputtered specimens. The fcc solid solution showed high phase stability against irradiation over a wide temperature range from 298 to 773 K, and remained as the main constituent phase even when the samples were irradiated up to 40 displacement per atom (dpa). Moreover, the irradiation did not seem to induce grain coarsening. This is the first report on the irradiation damage in 5-component HEA under MeV electron irradiation.     

A bat-neural network multi-agent system (BNNMAS) for stock price prediction: Case study of DAX stock price

Creating an intelligent system that can accurately predict stock price in a robust way has always been a subject of great interest for many investors and financial analysts. Predicting future trends of financial markets is more remarkable these days especially after the recent global financial crisis. So traders who access to a powerful engine for extracting helpful information throw raw data can meet the success. In this paper we propose a new intelligent model in a multi-agent framework called bat-neural network multi-agent system (BNNMAS) to predict stock price. The model performs in a four layer multi-agent framework to predict eight years of DAX stock price in quarterly periods. The capability of BNNMAS is evaluated by applying both on fundamental and technical DAX stock price data and comparing the outcomes with the results of other methods such as genetic algorithm neural network (GANN) and some standard models like generalized regression neural network (GRNN), etc. The model tested for predicting DAX stock price a period of time that global financial crisis was faced to economics. The results show that BNNMAS significantly performs accurate and reliable, so it can be considered as a suitable tool for predicting stock price specially in a long term periods.     

Thermal and transport properties of as-grown Ni-rich TiNi shape memory alloys

Electrical resistivity, Seebeck coefficient, specific heat and thermal conductivity measurements on the Ti_50−xNi_50+x (x = 0.0–1.6 at.%) shape memory alloys are performed to investigate their thermal and transport properties. In this study, anomalous features are observed in both cooling and heating cycles in all measured physical properties of the slightly Ni-rich TiNi alloys (x ≤ 1.0), corresponds to the transformation between the B19′ martensite and B2 austenite phases. Besides, the transition temperature is found to decrease gradually with increasing Ni content, and the driving force for the transition is also found to diminish slowly with the addition of excess Ni, as revealed by specific heat measurements. While the signature of martensitic transformation vanishes for the Ni-rich TiNi alloys with x ≥ 1.3, the characteristics of strain glass transition start to appear. The Seebeck coefficients of these TiNi alloys were found to be positive, suggesting the hole-type carriers dominate the thermoelectric transport. From the high-temperature Seebeck coefficients, the estimated value of Fermi energy ranges from ∼1.5 eV (Ti_48.4Ni_51.6) to ∼2.1 eV (Ti₅₀Ni₅₀), indicating the metallic nature of these alloys. In addition, the thermal conductivity of the slightly Ni-rich TiNi alloys with x ≤ 1.0 shows a distinct anomalous feature at the B19′ → B2 transition, likely due to the variation in lattice thermal conductivity.     

The Interplay of Modulus,Strength, and Ductility in Adhesive Design Using Biomimetic Polymer Chemistry

High‐performance adhesives require mechanical properties tuned to demands of the surroundings. A mismatch in stiffness between substrate and adhesive leads to stress concentrations and fracture when the bonding is subjected to mechanical load. Balancing material strength versus ductility, as well as considering the relationship between adhesive modulus and substrate modulus, creates stronger joints. However, a detailed understanding of how these properties interplay is lacking. Here, a biomimetic terpolymer is altered systematically to identify regions of optimal bonding. Mechanical properties of these terpolymers are tailored by controlling the amount of a methyl methacrylate stiff monomer versus a similar monomer containing flexible poly(ethylene glycol) chains. Dopamine methacrylamide, the cross‐linking monomer, is a catechol moiety analogous to 3,4‐dihydroxyphenylalanine, a key component in the adhesive proteins of marine mussels. Bulk adhesion of this family of terpolymers is tested on metal and plastic substrates. Incorporating higher amounts of poly(ethylene glycol) into the terpolymer introduces flexibility and ductility. By taking a systematic approach to polymer design, the region in which material strength and ductility are balanced in relation to the substrate modulus is found, thereby yielding the most robust joints.